ASTM F519-12a
- Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments
- standard by ASTM International, 11/15/2012
- Publisher: ASTM
$30.00$60.00
This test method specifies the use of air melted AISI E4340 steel per SAE AMS-S-5000 (formerly MIL-S-5000) heat treated to 260 to 280 ksi (pounds per square inch x 1000) as the baseline. This combination of alloy and heat treat level has been used for many years and a large database has been accumulated in the aerospace industry on its specific response to exposure to a wide variety of maintenance chemicals, or electroplated coatings, or both. Components with ultimate strengths higher than 260 to 280 ksi may not be represented by the baseline. In such cases, the cognizant engineering authority shall determine the need for manufacturing specimens from the specific material and heat treat condition of the component.
Related Products
ASTM F2690-08
Standard Guide for Suggested Procedures for Applying for a Flight Authority for an Unmanned Aircraft..
$26.00 $52.80
ASTM E1384-02
Standard Guide for Content and Structure of the Electronic Health Record (EHR)..
$55.00 $110.40
ASTM A653/A653M-09
Standard Specification for Steel Sheet, Zinc-Coated (Galvanized) or Zinc-Iron Alloy-Coated (Galvanne..
$30.00 $60.00
ASTM D6873-08
Standard Practice for Bearing Fatigue Response of Polymer Matrix Composite Laminates..
$21.00 $41.00